Dispersion particle size was measured by Zetasizer Nano ZS90 (Malvern Instruments Limited, Malvern, UK). The synthesized AuNPs were freeze dried, powdered, and used for X-ray diffraction (XRD) analysis. The spectra were evaluated using an X-ray diffractometer (PHILIPS X’Pert-MPD diffractometer, Amsterdam, the Netherlands) and Cu-Kα radiation (1.5405 Å) over an angular range of 10° to 80° at 40 kV and 30 mA.

The dried powder was diluted with potassium bromide at a the ratio of 1:100, and the results were recorded using the Fourier transform infrared spectroscopy find more (FTIR; PerkinElmer Inc., Walham, MA, USA) and spectrum GX spectrometry within the range of 500 to 4,000 cm-1. Transmission electron microscopy (TEM, JEM-1200EX, JEOL Ltd., Tokyo, Japan) was used to determine the size and morphology of AuNPs. AuNPs were prepared by dropping a small amount of aqueous

dispersion on copper grids, which were dried and then examined in the TEM. Further, the presence of Au metals in the sample was analyzed JNK-IN-8 mouse by energy dispersive X-ray analysis (EDX) combined with a field emission SEM. Cell culture MDA-MB-231 human breast cancer cells were kindly provided by Kyung Jin Lee, Institute for Life Sciences, ASAN Medical Center, University of Ulsan College of Medicine. MDA-MB-231 breast cancer cell lines were grown adherently and maintained in DMEM containing 10% fetal calf serum (FCS) and 1% antibiotic solution containing penicillin and streptomycin at 37°C under 5% CO2. All the experiments were performed in six-well plates, unless stated otherwise. Cells

were seeded onto plates at a density of 1 × 106 cells per well and Milciclib research buy incubated for 24 h prior to the experiments. The cells were washed with phosphate buffered saline (PBS, pH 7.4) and incubated in fresh medium containing different concentrations of AuNPs dissolved in water. Cell viability assay In order to evaluate the biocompatibility of the as-prepared AuNPs, we carried out cell viability assay in breast cancer cells (MDA-MB-231) by using MTT reagents. In addition, to compare the biocompatibility effect of bio-AuNPs, we used chemical-mediated synthesis of chem-AuNPs as a positive control. Cell viability was measured using the 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide dye reduction assay Liothyronine Sodium performed to determine the cytotoxic effect of the AuNPs at various concentrations. Briefly, the cells were plated onto 96-well flat-bottom culture plates with various concentrations of AuNPs (0 to100 μM). All the cultures were incubated for 24 h at 37°C in a humidified incubator. After 24 h of incubation (37°C, 5% CO2 in a humid atmosphere), 10 μL of MTT (5 mg/mL in PBS) was added to each well, and the plate was incubated for another 4 h at 37°C. The resulting formazan was dissolved in 100 μL of DMSO with gentle shaking at 37°C, and the absorbance was measured at 595 nm by using an ELISA reader (Spectra MAX; Molecular Devices, Sunnyvale, CA, USA).